Cathode active material for lithium secondary battery

ABSTRACT

Provided is a cathode active material which is lithium transition metal oxide having an α-NaFeO 2  layered crystal structure, wherein the transition metal is a blend of Ni and Mn, an average oxidation number of the transition metals except lithium is +3 or higher, and lithium transition metal oxide satisfies the Equation m(Ni)≧m(Mn) (in which m (Ni) and m (Mn) represent an molar number of manganese and nickel, respectively). The lithium transition metal oxide has a uniform and stable layered structure through control of oxidation number of transition metals to a level higher than +3, thus advantageously exerting improved overall electrochemical properties including electric capacity, in particular, superior high-rate charge/discharge characteristics.

CROSS REFERENCE TO RELATED APPLICATIONS

This application is a Continuation of PCT International Application No. PCT/KR2010/002202 filed on Apr. 9, 2010, which claims the benefit of Patent Application No. 10-2009-0031032 filed in Republic of Korea, on Apr. 9, 2009. The entire contents of all of the above applications is hereby incorporated by reference into the present application.

TECHNICAL FIELD

The present invention relates to a cathode active material for lithium secondary batteries. More specifically, the present invention relates to a cathode active material which is a lithium transition metal oxide having a layered crystal structure, wherein the transition metal is a blend of Ni and Mn, an average oxidation number of the transition metals except lithium is +3 or higher, and nickel content is comparable to or higher than manganese content, based on the molar ratio of transition metals. The lithium transition metal oxide has a stable layered structure with a uniform crystal shape through control of the oxidation number of transition metals, thus exerting superior rate characteristics under high-rate charge/discharge conditions as well as improved overall electrochemical properties.

BACKGROUND ART

Technological development and increased demand for mobile equipment have led to a rapid increase in the demand for secondary batteries as energy sources. Among these secondary batteries, lithium secondary batteries having high energy density and voltage, long cycle span and low self-discharge are commercially available and widely used.

In addition, increased interest in environmental issues has brought about a great deal of research associated with electric vehicles, hybrid electric vehicles and plug-in hybrid electric vehicles which alternate vehicles using fossil fuels such as gasoline vehicles and diesel vehicles. These electric vehicles generally use nickel-metal hydride secondary batteries as power sources. However, a great deal of study associated with use of lithium secondary batteries with high energy density and discharge voltage is currently underway and some of them are commercially available.

Meanwhile, the lithium secondary batteries generally use lithium cobalt composite oxide (LiCoO₂) as a cathode active material. Also, the use of lithium-manganese composite oxides such as LiMnO₂ having a layered crystal structure and LiMn₂O₄ having a spinel crystal structure and lithium nickel composite oxide (LiNiO₂) as the cathode active material has been considered.

Among these cathode active materials, LiCoO₂ is the most generally used owing to superior physical properties such as long life span and good charge/discharge characteristics, but has low structural stability and is costly due to natural resource limitations of cobalt used as a raw material, thus disadvantageously having limited price competiveness.

Lithium manganese oxides such as LiMnO₂ and LiMn₂O₄ have advantages of superior thermal stability and low costs, but have disadvantages of low capacity and bad low-temperature characteristics.

In addition, LiMnO₂-based cathode active materials are relatively cheap and exhibit higher discharge characteristics, but are disadvantageously difficult to synthesize and are unstable.

In order to solve the afore-mentioned problems, the present invention provides a low-cost highly functional cathode active material comprising lithium transition metal composite oxide wherein constituent elements satisfy the requirements including predetermined composition and oxidation number conditions, as mentioned below.

In this regard, U.S. Pat. No. 6,964,828 discloses a lithium transition metal oxide having a structure of Li(M1_((1-x))-Mn_(x))O₂ wherein M1 is a metal other than Cr, and each Ni has an oxidation number of +2, each Co has an oxidation number of +3, and each Mn has an oxidation number of +4, provided that M1 is Ni or Co.

In addition, Korean Patent Laid-open No. 2005-0047291 suggests a lithium transition metal oxide wherein Ni and Mn are present in equivalents amounts and have an oxidation number of +2 and +4, respectively.

As another example, Korean Patent No. 0543720 discloses a lithium transition metal oxide wherein Ni and Mn are present in substantially equivalent amounts, Ni has an oxidation number of 2.0 to 2.5 and Mn has an oxidation number of 3.5 to 4.0. This patent discloses that Ni and Mn should substantially have an oxidation number of +2 and +4, respectively, and that lithium batteries are deteriorated in properties, unless Ni and Mn have an oxidation number of +2 and +4, respectively, as apparent from Examples and Comparative Examples.

Also, Japanese Patent Application Publication No. 2001-0083610 discloses a lithium transition metal oxide which is represented by a structure of Li((Li(Ni_(1/2)Mn_(1/2))_((1-x)))O₂ or Li((Li_(x)(Ni_(y)Mn_(y)Co_(P))_((1-x)))O₂ and contains Ni and Mn in equivalent amounts. In accordance with the application, provided that Ni and Mn are present in identical amounts, Ni and Mn form Ni²⁺ and Mn⁴⁺, respectively, realizing structural stability and thus providing the desired layered structure.

Accordingly, in accordance with the prior art, the average oxidation number of transition metals should be +3, which is mentioned in U.S. Pat. No. 7,314,682. In this patent, the inventors disclose lithium transition metal oxide represented by the structure of Li_((2+2x)/(2+x))M′_(2x(2+x)/(2+x))M_((2−x)/(2+x))O_(2−δ) wherein M′ is an element having an average oxidation number of +3, in which M′ is not Li, and M is a transition metal having an average oxidation number of +3.

As can be confirmed from the afore-mentioned related patents, it was conventionally believed that (i) transition metals should have an average oxidation number of +3 in order to impart a stable layered structure to lithium transition metal oxide, and (ii) Ni present in an amount equivalent to Mn⁴⁺ should have an oxidation number of +2 in order to impart superior electrochemical properties to the lithium transition metal oxide, based on the premise (i).

However, the inventors of the present application confirmed that, in the case where Mn⁴⁺ and Ni²⁺ are simply selected to obtain an average oxidation number of +3, Ni²⁺ or the like is transferred to reversible Li sites, the problem, deterioration in electrochemical properties, cannot be solved.

Meanwhile, U.S. Pat. Nos. 7,078,128 and 7,135,252 suggest materials wherein Mn is present in an amount higher than that of Ni. However, the inventors of the present invention confirmed that a high amount of Mn cannot change an oxidation number of Mn⁴⁺ upon Li-charging and thus causes a decrease in capacity.

DISCLOSURE Technical Problem

Therefore, the present invention has been made to solve the above problems and other technical problems that have yet to be resolved and it is one aspect of the present invention to provide a cathode active material with superior structural and electrochemical properties.

As a result of a variety of extensive and intensive studies and experiments to solve the problems as described above, the inventors of the present invention have discovered that in the case where a cathode active material based on a lithium transition metal oxide having a layered crystal structure wherein the transition metal has an average oxidation number higher than +3 and nickel is present in an amount equivalent to that of manganese, the cathode active material has a complete crystal structure, thus considerably improving high-rate charge/discharge characteristics. The present invention was completed based on this discovery.

Technical Solution

Accordingly, the cathode active material for lithium secondary batteries is a lithium transition metal oxide which has a layered crystal structure, wherein the transition metal is a blend of Ni and Mn, and an average oxidation number of the transition metals except lithium is +3 or higher, and satisfies Equation 1 below: m(Ni)≧m(Mn)  (1)

wherein m (Ni) and m (Mn) represent a molar number of manganese and nickel, respectively.

In a preferred embodiment, the layered crystal structure is an α-NaFeO₂ layered crystal structure.

As mentioned above, it was known in the art that presence of Ni²⁺ and Mn⁴⁺ in equivalent amounts makes an average oxidation number of transition metal ions +3, thereby obtaining a desired layered structure. However, since Ni²⁺ has a size substantially similar to Li⁺, it moves to the lithium layer and readily forms a sodium salt, thus disadvantageously causing deterioration in electrochemical properties.

Accordingly, the inventors of the present invention conducted a great deal of research to prepare a cathode active material which has a stable layered crystal structure and exhibits superior capacity and rate characteristics. As a result, the inventors discovered that the stable layered crystal structure depends on the size difference between the lithium ion and the transition metal ion, rather than Ni²⁺ and Mn⁴⁺.

Specifically, the inventors confirmed that lithium composite transition metal oxide having a layered crystal structure of α-NaFeO₂ is divided into a lithium-containing Li-oxide layer (referred to as a “lithium layer”) and a transition metal-containing transition metal oxide layer (referred to as an “MO layer”). As the size difference between the ions constituting respective layers, that is, the lithium and transition metal ions, increases, the two layers can be readily separated and developed.

The inventors of the present invention thoroughly tried to accomplish the desired layered crystal structure. As a result, the inventors confirmed that the size difference between the ions is expressed by the bonding distance between each ion and the oxygen ion or bonding force therebetween, and as a metal having cationic characteristics has an increased oxidation number, it has a decreased ionic diameter. In addition, the inventors considered that the difference between the MO layer and the lithium layer can be increased by increasing the oxidation number of transition metals. This expectation was confirmed through a great deal of experiments.

The principle that the layered crystal structure can be suitably developed through increased size difference between the lithium ion and the transition metal ion by increasing the average oxidation number of transition metal to a level higher than +3 is in contrast to the conventional idea accepted in the art that the average oxidation number of transition metals should be adjusted to +3 to stabilize the layered crystal structure.

The inventors of the present invention predicted that the best method to increase the oxidation number of transition metals would be to adjust the total average oxidation number to +3 or higher by decreasing the amount of Ni²⁺, which can be readily permeated into the lithium layer. This prediction is based on the idea that the amount of Ni³⁺ having a size smaller than Ni²⁺ increases, thus causing an increase in size difference between the ions.

Meanwhile, the cathode active material according to the present invention, as mentioned above, contains nickel and manganese wherein nickel is present in an amount equivalent to or higher than manganese. When the content of manganese is higher than that of nickel, capacity is disadvantageously decreased. On the other hand, the cathode active material of the present invention solves this problem.

In a preferred embodiment, the cathode active material of the present invention may optionally comprise, in addition to nickel and manganese, cobalt.

In this case, regarding the composition of transition metals present in the cathode active material, for example, based on the molar ratio of the transition metals, the nickel content is 0.3 to 0.9, and the manganese content is 0.1 to 0.5 under the condition of Equation 1, and the cobalt content is 0.0 to 0.4. The composition of transition metals which can realize superior properties when practically applied to batteries is only provided for illustration and the improvement in properties is not limited to the composition.

Hereinafter, the present invention will be described in detail. The cathode active material according to the present invention is lithium transition metal oxide wherein (i) the average oxidation number of transition metals except lithium is higher than +3 and (ii) nickel is present in an amount equivalent to or higher than manganese.

Advantageously, such lithium transition metal oxide can considerably decrease the amount of transition metals present in the lithium layer, based on the stable crystal structure of the cathode active material by maintaining the average oxidation number of transition metals to a level higher than +3, thus improving mobility and rate characteristics of lithium ions, as well as capacity.

Regarding the aspect (i), the cathode active material of the present invention has an average oxidation number of transition metals except lithium, higher than +3, thus decreasing an average size of transition metal ions, increasing the size difference between lithium ions, and promoting separation between layers, thereby forming a stable layered crystal structure.

When the average oxidation number of transition metals is excessively increased, electric charges capable of moving lithium ions are decreased, thus disadvantageously decreasing capacity. Preferably, the average oxidation number of transition metals is higher than 3.0 and not higher than 3.5, more preferably, 3.01 to 3.3, more particularly preferably, 3.1 to 3.3.

In this case, the total average oxidation number of Mn and Ni corresponding thereto is 3.0 to 3.5, preferably, 3.1 to 3.3.

Regarding the aspect (ii), the cathode active material according to the present invention is composed of nickel and manganese wherein the content of nickel is equivalent to or higher than that of manganese, on a molar basis, as represented by Equation 1 below: m(Ni)≧m(Mn)  (1)

When nickel is present in an amount higher than manganese, nickel in an amount corresponding to the difference between the nickel content and the manganese content, is changed to Ni³⁺, thus decreasing ion size. Accordingly, the average size difference between the lithium ion and the transition metal ion increases, thus minimizing permeation of Ni²⁺ into the lithium layer, and improving stability of the layered crystal structure.

On the other hand, when manganese is present in an amount higher than nickel, +4 ions which do not contribute to charging/discharging are increased and capacity is thus decreased.

As mentioned above, in the case where the cathode active material according to the present invention contains excessive nickel, as compared to manganese, the nickel is divided into nickel (a) present in an excessive amount, as compared to the manganese content and nickel (b) present in an amount corresponding to the manganese content.

Preferably, the nickel (a) is Ni³⁺, and the nickel (b) contains Ni²⁺ and Ni³⁺.

As such, for the cathode active material according to the present invention, the nickel content is equivalent to or higher than the manganese content, an average oxidation number of transition metals is higher than +3, the size difference between the lithium ion and the transition metal ion increases, layer separation is promoted and permeation of Ni²⁺ into the lithium layer can be minimized. For the cathode active material, the content of nickel inserted into the lithium site may be lower than 5 mol %.

Preferably, the cathode active material contains Ni²⁺ and Mn⁴⁺ wherein Ni²⁺ is present in an amount smaller than Mn⁴⁺.

Specifically, as represented by Equation 2 below, a molar ratio of Mn⁴⁺ to Ni²⁺, i.e., m(Ni²⁺)/m(Mn⁴⁺), is 0.4 to 1. That is, the content of Ni²⁺ is not equivalent to the content of Mn⁴⁺, and the content of Ni²⁺ is smaller than that of Mn⁴⁺. 0.4<m(Ni²⁺)/m(Mn⁴⁺)<1  (2)

When the m(Ni²⁺)/m(Mn⁴⁺) is 1 or higher, an increase in average oxidation number of transition metals is not obtained and thus size difference between the ions cannot be induced. When m(Ni²⁺)/m(Mn⁴⁺) is less than 0.4, an oxidation number of transition metals is excessively increased, and the amount of electric charges to be moved is decreased and capacity is thus decreased. When m(Ni²⁺)/m(Mn⁴⁺) is 0.4 to 0.9, more superior electrochemical properties can be obtained.

For the lithium transition metal oxide of the present invention, transition metals comprising nickel, manganese and optionally cobalt can be partially substituted with other metal element(s), preferably the transition metals can be substituted in a small amount not higher than 5% by metals or cationic elements, so long as the layered crystal structure can be maintained. It is apparent that this case is included within the scope so long as it satisfies the properties of the present invention.

In addition to the lithium transition metal oxide according to the present invention, the cathode active material may comprise general lithium transition metal oxide which does not satisfy the conditions. The general lithium transition metal oxide includes all oxides composed of one or more of Ni, Co and Mn, for example, lithium transition metal oxides known in the art. Such a composite-type cathode active material comprises lithium transition metal oxide according to the present invention in an amount of at least 30 wt %, preferably at least 50 wt %.

The present invention provides a positive electrode comprising the cathode active material and a lithium secondary battery comprising the positive electrode. Hereinafter, the positive electrode is simply referred to as a “cathode”.

The lithium secondary battery generally comprises a cathode, an anode, a separator, and a lithium salt-containing non-aqueous electrolyte.

For example, the cathode is prepared by applying a cathode mix comprising a cathode active material, a conductive material, a binder and a filler to a cathode current collector, followed by drying. The cathode mix may comprise a filler, if necessary.

The cathode current collector is generally fabricated to have a thickness of 3 to 500 μm. There is no particular limit to the cathode current collector, so long as it has suitable conductivity without causing adverse chemical changes in the fabricated battery. As examples of the cathode current collector, mention may be made of stainless steel, aluminum, nickel, titanium, sintered carbon, and aluminum or stainless steel surface-treated with carbon, nickel, titanium, silver or the like. If necessary, these current collectors may also be processed to form fine irregularities on the surface thereof so as to enhance adhesion to the cathode active materials. In addition, the current collectors may be used in various forms including films, sheets, foils, nets, porous structures, foams and non-woven fabrics.

The conductive material is commonly added in an amount of 1 to 20% by weight, based on the total weight of the mixture including the cathode active material. Any conductive material may be used without particular limitation so long as it has suitable conductivity without causing adverse chemical changes in the fabricated secondary battery. As examples of the conductive materials that can be used in the present invention, mention may be made of conductive materials, including graphite such as natural or artificial graphite; carbon blacks such as carbon black, acetylene black, Ketjen black, channel black, furnace black, lamp black and thermal black; conductive fibers such as carbon fibers and metallic fibers; metallic powders such as carbon fluoride powder, aluminum powder and nickel powder; conductive whiskers such as zinc oxide and potassium titanate; conductive metal oxides such as titanium oxide; and polyphenylene derivatives.

The binder is a component which enhances binding of an active material to a conductive material and current collector. The binder is commonly added in an amount of 1 to 20% by weight, based on the total weight of the compound including the anode active material. Examples of the binder include polyvinylidene, polyvinyl alcohol, carboxymethylcellulose (CMC), starch, hydroxypropylcellulose, regenerated cellulose, polyvinyl pyrollidone, tetrafluoroethylene, polyethylene, polypropylene, ethylene propylene diene terpolymer (EPDM), sulfonated EPDM, styrene butadiene rubber, fluoro rubber and various copolymers.

The filler is a component used to inhibit expansion of the cathode. There is no particular limit to the filler, so long as it does not cause adverse chemical changes in the fabricated battery and is a fibrous material. As examples of the filler, there may be used olefin polymers such as polyethylene and polypropylene; and fibrous materials such as glass fibers and carbon fibers.

For example, the anode is prepared by applying an anode active material to an anode current collector, followed by drying. The anode active material may further comprise the afore-mentioned ingredients, i.e., the conductive material, the binder and the filler.

The anode current collector is generally fabricated to have a thickness of 3 to 500 μm. There is no particular limit to the anode current collector, so long as it has suitable conductivity without causing adverse chemical changes in the fabricated battery. As examples of the anode current collector, mention may be made of copper, stainless steel, aluminum, nickel, titanium, sintered carbon, and copper or stainless steel surface-treated with carbon, nickel, titanium or silver, and aluminum-cadmium alloys. Similar to the cathode current collector, if necessary, these current collectors may also be processed to form fine irregularities on the surface thereof so as to enhance adhesion to the anode active materials. In addition, the current collectors may be used in various forms including films, sheets, foils, nets, porous structures, foams and non-woven fabrics.

In addition, examples of anode active materials that can be used in the present invention include carbons such as hard carbons and graphite carbons; metal composite oxides such as Li_(y)Fe₂O₃ (0≦y≦1), Li_(y)WO₂ (0≦y≦1), Sn_(x)Me_(1-x)Me′_(y)O_(z) (Me: Mn, Fe, Pb, Ge; Me′: Al, B, P, Si, Group I, II and III elements of the Periodic Table, halogens; 0<x≦1; 1≦y≦3; 1≦z≦8); lithium metals; lithium alloys; silicon-based alloys; tin-based alloys; metal oxides such as SnO, SnO₂, PbO, PbO₂, Pb₂O₃, Pb₃O₄, Sb₂O₃, Sb₂O₄, Sb₂O₅, GeO, GeO₂, Bi₂O₃, Bi₂O₄, Bi₂O₅ and the like; conductive polymers such polyacetylene; and Li—Co—Ni materials.

The separator is interposed between the cathode and anode. As the separator, an insulating thin film having high ion permeability and mechanical strength is used. The separator typically has a pore diameter of 0.01 to 10 μm and a thickness of 5 to 300 μm. As the separator, sheets or non-woven fabrics made of an olefin polymer such as polypropylene and/or glass fibers or polyethylene, which have chemical resistance and hydrophobicity, are used. When a solid electrolyte such as a polymer is employed as the electrolyte, the solid electrolyte may also serve as both the separator and electrolyte.

The lithium salt-containing, non-aqueous electrolyte is composed of a non-aqueous electrolyte and a lithium salt. As the non-aqueous electrolyte, a non-aqueous electrolytic solution, solid electrolyte and inorganic solid electrolyte may be utilized.

As the non-aqueous electrolytic solution that can be used in the present invention, for example, mention may be made of non-protic organic solvents such as N-methyl-2-pyrollidinone, propylene carbonate, ethylene carbonate, butylene carbonate, dimethyl carbonate, diethyl carbonate, gamma-butyrolactone, 1,2-dimethoxy ethane, tetrahydroxy Franc, 2-methyl tetrahydrofuran, dimethylsulfoxide, 1,3-dioxolane, formamide, dimethylformamide, dioxolane, acetonitrile, nitromethane, methyl formate, methyl acetate, phosphoric acid triester, trimethoxy methane, dioxolane derivatives, sulfolane, methyl sulfolane, 1,3-dimethyl-2-imidazolidinone, propylene carbonate derivatives, tetrahydrofuran derivatives, ether, methyl propionate and ethyl propionate.

As examples of the organic solid electrolyte utilized in the present invention, mention may be made of polyethylene derivatives, polyethylene oxide derivatives, polypropylene oxide derivatives, phosphoric acid ester polymers, poly agitation lysine, polyester sulfide, polyvinyl alcohols, polyvinylidene fluoride, and polymers containing ionic dissociation groups.

As examples of the inorganic solid electrolyte utilized in the present invention, mention may be made of nitrides, halides and sulfates of lithium such as Li₃N, LiI, Li₅NI₂, Li₃N—LiI—LiOH, LiSiO₄, LiSiO₄—LiI—LiOH, Li₂SiS₃, Li₄SiO₄, Li₄SiO₄—LiI—LiOH and Li₃PO₄—Li₂S—SiS₂.

The lithium salt is a material that is readily soluble in the above-mentioned non-aqueous electrolyte and may include, for example, LiCl, LiBr, LiI, LiClO₄, LiBF₄, LiB₁₀Cl₁₀, LiPF₆, LiCF₃SO₃, LiCF₃CO₂, LiAsF₆, LiSbF₆, LiAlCl₄, CH₃SO₃Li, CF₃SO₃Li, (CF₃SO₂)₂NLi, chloroborane lithium, lower aliphatic carboxylic acid lithium, lithium tetraphenyl borate and imide.

Additionally, in order to improve charge/discharge characteristics and flame retardancy, for example, pyridine, triethylphosphite, triethanolamine, cyclic ether, ethylenediamine, n-glyme, hexaphosphoric triamide, nitrobenzene derivatives, sulfur, quinone imine dyes, N-substituted oxazolidinone, N,N-substituted imidazolidine, ethylene glycol dialkyl ether, ammonium salts, pyrrole, 2-methoxy ethanol, aluminum trichloride or the like may be added to the non-aqueous electrolyte. If necessary, in order to impart incombustibility, the non-aqueous electrolyte may further include halogen-containing solvents such as carbon tetrachloride and ethylene trifluoride. Further, in order to improve high-temperature storage characteristics, the non-aqueous electrolyte may additionally include carbon dioxide gas.

The lithium secondary batteries may be used as unit batteries of battery modules which are power sources of medium-large devices requiring long cycles and high-rate charge/discharge characteristics.

Preferably, examples of medium-large devices include, but are not limited thereto, power tools driven by battery-powered motors; electric vehicles (EVs) including hybrid electric vehicles (HEVs) and plug-in hybrid electric vehicles (PHEVs); electric two-wheeled vehicles including E-bikes and E-scooters; and electric golf carts.

Accordingly, the present invention provides a medium-large battery pack including the lithium secondary batteries as units. The general structure and fabrication method of medium-large battery packs are known in the art and a detailed explanation thereof is thus omitted.

Advantageous Effects

As apparent from the fore-going, the present invention provides a cathode active material which is based on lithium transition metal oxide having a layered crystal structure, wherein the transition metal is a blend of Ni and Mn, an average oxidation number of transition metals except lithium is +3 or higher, and nickel content is comparable to or higher than manganese content, thus realizing a stable crystal structure and considerably superior high-rate charge/discharge characteristics.

Best Mode

Now, the present invention will be described in more detail with reference to the following Examples. These examples are provided only for illustrating the present invention and should not be construed as limiting the scope and spirit of the present invention.

Comparative Example 1

For the total transition metal salts, a molar ratio of a cobalt salt was adjusted to 8 mol % and a molar ratio of nickel salt and manganese salt (Ni/Mn) was adjusted to 1.24. Then, all transition metal salts were dissolved in distilled water to obtain a transition metal composite, while elevating the basicity of the aqueous transition metal solution. The solvent was removed from the transition metal composite via vacuum filtration, dried in an oven at 115° C. for 16 hours to remove the remaining solvent, the lithium salt was mixed such that the molar ratio of Ni²⁺/Mn⁴⁺ was adjusted to 1, heated in an electric furnace at an elevating rate of 300° C./hour to about 950° C. and sintered at this temperature for 10 hours to obtain a lithium transition metal composite oxide.

Example 1

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 1 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.88.

Example 2

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 1 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.76.

Example 3

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 1 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.64.

Example 4

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 1 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.52.

Example 5

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 1 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.41.

Comparative Example 2

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 1 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.29.

Comparative Example 3

For the total transition metal salts, a molar ratio of a cobalt salt was adjusted to 8 mol % and a molar ratio of nickel salt and manganese salt (Ni/Mn) was adjusted to 1.24. Then, all transition metal salts were dissolved in distilled water to obtain transition metal composite, while elevating the basicity of the aqueous transition metal solution. The solvent was removed from the transition metal composite via vacuum filtration, dried in an oven at 115° C. for 16 hours to remove the remaining solvent, the lithium salt was mixed such that the molar ratio of Ni²⁺/Mn⁴⁺ was adjusted to 1, heated in an electric furnace at an elevating rate of 300° C./hour to about 960° C. and sintered at this temperature for 10 hours to obtain lithium transition metal composite oxide.

Example 6

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 3 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.88.

Example 7

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 3 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.76.

Example 8

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 3 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.64.

Example 9

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 3 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.52.

Example 10

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 3 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.41.

Comparative Example 4

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 3 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.29.

Comparative Example 5

For the total transition metal salts, a molar ratio of a cobalt salt was adjusted to 8 mol % and a molar ratio of nickel salt and manganese salt (Ni/Mn) was adjusted to 1.24. Then, all transition metal salts were dissolved in distilled water to obtain a transition metal composite, while elevating the basicity of the aqueous transition metal solution. The solvent was removed from the transition metal composite via vacuum filtration, dried in an oven at 115° C. for 16 hours to remove the remaining solvent, the lithium salt was mixed such that the molar ratio of Ni²⁺/Mn⁴⁺ was adjusted to 1, heated in an electric furnace at an elevating rate of 300° C./hour to about 970° C. and sintered at this temperature for 10 hours to obtain lithium transition metal composite oxide.

Example 11

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 5 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.88.

Example 12

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 5 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.76.

Example 13

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 5 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.64.

Example 14

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 5 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.52.

Example 15

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 5 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.41.

Comparative Example 6

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 5 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.29.

Comparative Example 7

For the total transition metal salts, a molar ratio of a cobalt salt was adjusted to 8 mol % and a molar ratio of nickel salt and manganese salt (Ni/Mn) was adjusted to 1.24. Then, all transition metal salts were dissolved in distilled water to obtain transition metal composite, while elevating the basicity of the aqueous transition metal solution. The solvent was removed from the transition metal composite via vacuum filtration, dried in an oven at 115° C. for 16 hours to remove the remaining solvent, the lithium salt was mixed such that the molar ratio of Ni²⁺/Mn⁴⁺ was adjusted to 1, heated in an electric furnace at an elevating rate of 300° C./hour to about 980° C. and sintered at this temperature for 10 hours to obtain lithium transition metal composite oxide.

Example 16

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 7 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.88.

Example 17

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 7 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.76.

Example 18

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 7 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.64.

Example 19

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 7 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.52.

Example 20

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 7 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.41.

Comparative Example 8

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 7 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.29.

Comparative Example 9

For the total transition metal salts, a molar ratio of a cobalt salt was adjusted to 8 mol % and a molar ratio of nickel salt and manganese salt (Ni/Mn) was adjusted to 1.24. Then, all transition metal salts were dissolved in distilled water to obtain transition metal composite, while elevating the basicity of the aqueous transition metal solution. The solvent was removed from the transition metal composite via vacuum filtration, dried in an oven at 115° C. for 16 hours to remove the remaining solvent, the lithium salt was mixed such that the molar ratio of Ni²⁺/Mn⁴⁺ was adjusted to 1, heated in an electric furnace at an elevating rate of 300° C./hour to about 990° C. and sintered at this temperature for 10 hours to obtain lithium transition metal composite oxide.

Example 21

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 9 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.88.

Example 22

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 9 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.76.

Example 23

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 9 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.64.

Example 24

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 9 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.52.

Example 25

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 9 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.41.

Comparative Example 10

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 9 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.29.

Comparative Example 11

For the total transition metal salts, a molar ratio of a cobalt salt was adjusted to 8 mol % and a molar ratio of nickel salt and manganese salt (Ni/Mn) was adjusted to 1.24. Then, all transition metal salts were dissolved in distilled water to obtain transition metal composite, while elevating the basicity of the aqueous transition metal solution. The solvent was removed from the transition metal composite via vacuum filtration, dried in an oven at 115° C. for 16 hours to remove the remaining solvent, the lithium salt was mixed such that the molar ratio of Ni²⁺/Mn⁴⁺ was adjusted to 1, heated in an electric furnace at an elevating rate of 300° C./hour to about 1,000° C. and sintered at 950° C. for 10 hours to obtain lithium transition metal composite oxide.

Example 26

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 11 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.88.

Example 27

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 11 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.76.

Example 28

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 11 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.64.

Example 29

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 11 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.52.

Example 30

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 11 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.41.

Comparative Example 12

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 11 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 0.29.

Example 31

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 1 except that the molar ratio of nickel salt and manganese salt was 1.13.

Example 32

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 1 except that the molar ratio of nickel salt and manganese salt was 1.43.

Comparative Example 13

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 1 except that the molar ratio of nickel salt and manganese salt was 1, Co was not used and the sintering temperature was 1,000° C.

Comparative Example 14

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 13 except that the molar ratio of Ni²⁺/Mn⁴⁺ was 1.

Comparative Example 15

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 13 except that the molar ratio of nickel salt and manganese salt was 0.96.

Comparative Example 16

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 13 except that the molar ratio of nickel salt and manganese salt was 0.90.

Comparative Example 17

Lithium transition metal composite oxide was obtained in the same manner as in Comparative Example 13 except that the molar ratio of nickel salt and manganese salt was 0.82.

Experimental Example 1

The cathode active materials prepared in Examples 1 to 30 and Comparative Examples 1 to 17 were thoroughly mixed with NMP such that a weight ratio (wt %) of an active material:a conductive material:a binder was 95:2.5:2.5. The mixture thus obtained was applied to a 20 μm Al foil and dried at 130° C. to obtain a cathode. The cathode thus obtained was roll-pressed to have a porosity of about 25% and punched in the form of a coin with a diameter of 1.487 cm. Li-metal was used as the counter electrode of the punched cathode and a coin-shaped battery was obtained using an electrolyte solution of 1M LiPF6 in a mix solvent of EC:DMC:DEC=1:2:1.

The first cycle discharge capacity and efficiency of the battery were obtained through 0.1C charge/0.1C discharge, a ratio of 1C, 2C discharge capacity to 0.1C charge was calculated as a percentage, rate capability was measured and the results thus obtained are shown in Table 1 below:

TABLE 1 1^(st) cycle discharge 1^(st) cycle 1 C 2 C capacity efficiency discharge/0.1 C discharge/0.1 C (mAh/g) (%) discharge (%) discharge (%) Comp. Ex. 1 150.3 83.5 76.2 65.7 Ex. 1 162.1 86.9 85.1 80.3 Ex. 2 161.5 89.8 90.2 86.1 Ex. 3 162.3 90.3 91.2 86.4 Ex. 4 158.1 90.6 91.4 86.8 Ex. 5 154.6 91.2 92.3 87.2 Comp. Ex. 2 132.8 90.2 91.6 86.8 Comp. Ex. 3 148.2 84.5 73.2 65.9 Ex. 6 159.1 85.3 86.1 78.2 Ex. 7 160.2 89.0 89.6 85.5 Ex. 8 161.3 89.3 90.2 86.8 Ex. 9 157.5 89.5 91.4 86.4 Ex. 10 152.6 90.6 92.1 86.9 Comp. Ex. 4 130.5 91.2 91.8 87.2 Comp. Ex. 5 149.9 83.8 72.2 65.2 Ex. 11 160.1 87.3 86.1 80.2 Ex. 12 160.7 89.3 90.1 84.5 Ex. 13 162.1 89.8 89.7 85.9 Ex. 14 158.3 90.5 90.5 84.3 Ex. 15 154.6 90.3 91.1 86.9 Comp. Ex. 6 128.1 89.8 90.8 86.5 Comp. Ex. 7 143.6 81.3 69.3 62.5 Ex. 16 156.1 85.5 85.1 78.2 Ex. 17 158.6 86.5 88.5 83.3 Ex. 18 159.3 87.2 88.2 83.0 Ex. 19 157.3 86.9 89.0 83.8 Ex. 20 155.6 87.3 88.4 82.9 Comp. Ex. 8 123.4 86.4 88.2 83.4 Comp. Ex. 9 141.5 81.3 65.3 60.5 Ex. 21 155.3 84.5 84.2 75.5 Ex. 22 157.2 85.5 86.9 82.1 Ex. 23 157.6 85.6 86.2 82.6 Ex. 24 155.3 86.0 86.9 83.0 Ex. 25 153.6 86.2 87.8 82.4 Comp. Ex. 10 121.6 85.7 87.3 83.5 Comp. Ex. 11 138.2 81.3 60.3 52.2 Ex. 26 153.2 82.8 84.2 72.5 Ex. 27 154.8 83.0 84.8 79.1 Ex. 28 154.2 83.9 85.2 80.6 Ex. 29 150.3 84.2 85.3 80.7 Ex. 30 148.2 84.9 86.8 81.4 Comp. Ex. 12 118.6 84.7 85.9 81.7 Comp. Ex. 13 144.8 87.5 82.2 68.3 Comp. Ex. 14 130.2 84.3 70.1 53.6 Comp. Ex. 15 140.3 87.7 81.3 68.7 Comp. Ex. 16 132.9 86.9 81.6 67.4 Comp. Ex. 17 131.2 85.2 80.5 67.5

Experimental Example 2

The cathode active materials prepared in Examples 1 to 30 and Comparative Examples 1 to 12 were subjected to XRD, the structure thereof was analyzed through Retveld-refinement, a ratio of Ni (Ni²⁺) present in the Li site, a ratio of Ni³⁺ among nickel (b) corresponding to the manganese content was obtained and the results thus obtained are shown in Table 2 below.

TABLE 2 Average Average oxidation oxidation Ni in number of Ni³⁺ in number of lithium M(Ni²⁺)/m(Mn ⁴⁺) transition Ni(b) Mn and Ni layer expected measured metal (%) (b) (%) Comp. 1 1 3.00 0 3.00 5.33 Ex. 1  Ex. 1  0.88 0.86 3.05 11.4 3.06 4.22 Ex. 2  0.76 0.73 3.11 23.1 3.12 3.07 Ex. 3  0.64 0.60 3.16 35.2 3.18 2.25 Ex. 4  0.52 0.48 3.21 47.5 3.24 2.01 Ex. 5  0.41 0.40 3.25 59.1 3.30 1.55 Comp. 0.29 0.25 3.29 69.4 3.35 1.2 Ex. 2  Comp. 1 1 3 0 3 5.29 Ex. 3  Ex. 6  0.88 0.88 3.04 11.4 3.06 4.15 Ex. 7  0.76 0.72 3.12 23.3 3.12 3.02 Ex. 8  0.64 0.59 3.17 35.4 3.18 2.17 Ex. 9  0.52 0.48 3.2 47.6 3.24 2.06 Ex. 10 0.41 0.41 3.26 59.3 3.30 1.43 Comp. 0.29 0.24 3.25 68.6 3.32 1.23 Ex. 4  Comp. 1 1 3 0 3.00 5.68 Ex. 5  Ex. 11 0.88 0.86 3.03 11.4 3.05 4.28 Ex. 12 0.76 0.74 3.15 23.5 3.15 3.1 Ex. 13 0.64 0.59 3.17 35.4 3.18 2.3 Ex. 14 0.52 0.49 3.24 48.2 3.28 1.92 Ex. 15 0.41 0.42 3.28 59.7 3.32 1.57 Comp. 0.29 0.22 3.22 67.3 3.26 1.4 Ex. 6  Comp. 1 1 3 0.0 3.00 5.22 Ex. 7  Ex. 16 0.88 0.88 3.08 11.6 3.10 4.10 Ex. 17 0.76 0.75 3.16 23.6 3.16 2.98 Ex. 18 0.64 0.6 3.17 35.4 3.18 2.33 Ex. 19 0.52 0.48 3.22 47.9 3.26 1.85 Ex. 20 0.41 0.41 3.27 59.5 3.31 1.46 Comp. 0.29 0.27 3.38 71.1 3.42 1.12 Ex. 8  Comp. 1 1 3 0.0 3.00 5.12 Ex. 9  Ex. 21 0.88 0.87 3.07 11.6 3.09 4.12 Ex. 22 0.76 0.76 3.19 23.8 3.19 3.17 Ex. 23 0.64 0.61 3.18 35.5 3.19 2.28 Ex. 24 0.52 0.50 3.26 48.5 3.30 1.88 Ex. 25 0.41 0.42 3.3 60.0 3.34 1.36 Comp. 0.29 0.29 3.41 71.7 3.45 1.08 Ex. 10 Comp. 1 1 3 0.0 3.00 5.80 Ex. 11 Ex. 26 0.88 0.87 3.07 11.6 3.09 4.32 Ex. 27 0.76 0.73 3.11 23.2 3.11 3.21 Ex. 28 0.64 0.59 3.17 35.4 3.18 1.77 Ex. 29 0.52 0.49 3.21 47.8 3.25 1.53 Ex. 30 0.41 0.41 3.27 59.5 3.31 1.29 Ex. 31 0.76 0.72 3.12 24.6 3.12 2.71 Ex. 32 0.76 0.80 3.10 23.1 3.08 2.83 Comp. 0.29 0.25 3.29 69.2 3.33 1.10 Ex. 12

As can be seen from Tables 1 and 2 above, the cathode active materials according to the present invention exhibit a slight decrease in capacity due to a decrease in specific surface area as a function of temperature, but the layered crystal structure can be more stably formed by increasing the average oxidation number of transition metals to a level higher than 3+, regardless of variations in temperature, or elevating the oxidation number of Ni present in an amount equivalent to that of manganese. Also, it can be seen that electrochemical properties such as rate properties and one-cycle charge/discharge efficiency consistently increase, based on the definite principle regardless of conditions such as temperature.

This means that cathode active material of the present invention increases the oxidation number of the transition metal layer, thereby increasing the size difference between the lithium ion and the transition metal ion and thus improving structural stability and electrochemical properties. In addition, it can be seen that as compared to a conventional case wherein Ni is added in an amount equivalent to that of Mn, each Ni is Ni²⁺, the oxidation number of transition metals is +3 (See Comparative Examples 1, 3, 5, 7, 8 and 11), the present invention wherein the oxidation number of transition metal is adjusted to a level higher than +3 can efficiently stabilize the layered crystal structure.

In particular, even in the case where, for nickel (b) present in content comparable to the manganese content, Ni³⁺ is present in an amount of 50% of higher, the present invention exhibits superior electrochemical properties, as compared to Comparative Examples.

Meanwhile, Comparative Examples 13 to 17 wherein for the overall composition, Mn is present in an amount comparable to or higher than Ni exhibit a decrease in capacity, although is not excluded from the theoretically scientific principle of the present invention that the structure is stabilized and oxidation number of Ni present in an equivalent to the manganese content can be elevated by increasing the oxidation number of transition metals.

Although the preferred embodiments of the present invention have been disclosed for illustrative purposes, those skilled in the art will appreciate that various modifications, additions and substitutions are possible, without departing from the scope and spirit of the invention as disclosed in the accompanying claims. 

1. A cathode active material for lithium secondary batteries, wherein the cathode active material is lithium transition metal oxide having a layered crystal structure, wherein the layered crystal structure is an α-NaFeO₂ layered crystal structure, and wherein the transition metal is a blended transition metal of Ni and Mn, and an average oxidation number of transition metals except lithium is 3.03 to 3.3 and the lithium transition metal oxide satisfies Equation 1 below: m(Ni)≧m(Mn)  (1) wherein m (Ni) and m (Mn) represent a molar number of nickel salt and manganese salt, respectively.
 2. The cathode active material according to claim 1, wherein the lithium transition metal oxide further comprises cobalt.
 3. The cathode active material according to claim 1, wherein the average oxidation number of transition metals except lithium is 3.1 to 3.3.
 4. A cathode comprising the cathode active material according to claim
 1. 5. A lithium secondary battery comprising the cathode according to claim
 4. 